Tobacco stalks core-derived activated carbon with high capacitance by ZnCl2 for supercapacitors

Zhuwen Ma1 , Bixia Jiang2 , Qinghua Yuan3 , Lin Cao4 , Lan Liu5 , Junling Tian6 , Zhenrui Huang7 , Zhaohui Zong8 , Zhidan Lin9 , Peng Zhang10 , Jun Wang11

1, 3, 7Guangdong Provincial Engineering and Technology Research Center for Tobacco Breeding and Comprehensive Utilization; Crops Research Institute, Guangdong Academy of Agricultural Sciences; Guangdong Provincial Key Laboratory of Crop Genetic Improvement, Guangzhou, China

2, 4, 9, 10Institute of Advanced Wear and Corrosion Resistant and Functional Materials, Jinan University, Guangzhou, China

5, 6, 8, 11Nanxiong Institute of Tobacco Research, Nanxiong, China

11Corresponding author

Vibroengineering PROCEDIA, Vol. 39, 2021, p. 121-126.
Received 19 October 2021; received in revised form 29 October 2021; accepted 6 November 2021; published 2 December 2021

Copyright © 2021 Zhuwen Ma, et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Creative Commons License
Table of Contents Download PDF Acknowledgements References
Cite this article
Views 14
Reads 6
Downloads 71
CrossRef Citations 0

It is well known improper disposal of tobacco stalks as waste can cause great pollution to farmland and the environment. In this paper, tobacco-stalk-core-based activated carbon was successfully synthesized by pre-carbonization and ZnCl2 activation. The influences of different activator ratios on the microstructure and the electrochemical performance of the activated carbon were systematically investigated. The results showed that while the ratio of the activator to the precursor of carbon was 2:1, the specific capacitance was high to 342.0 F·g-1 at 1 A·g-1 current density. To sum up, an as-prepared carbon material with high capacitance could be obtained by tobacco stalks core. ZnCl2 is an effective activator for the reuse of tobacco stalk, and it provides a new way of technology for synthesizing tobacco waste recycling resources.

Keywords: tobacco stalks core, activated carbon, supercapacitor.

1. Introduction

In recent years, a growing number of researchers have explored the conversion of biomass/biomass waste into products with high added value [1]. According to statistics, there are many tobacco wastes every year in China, of which is about 1.20×106 tons, as the world's largest producer of tobacco [2]. Tobacco stalk waste is mostly burned, buried or discarded, which not only is the farmland damaged greatly, but also is the environment polluted seriously [3]. Consequently, the reuse of tobacco stalk waste as an environmentally friendly, easily available, low-cost and renewable carbon precursor will help curb pollution and increase its economic value.

At present, the precursors of activated carbon in the market are mainly coal, coke and biomass. Among these precursors, biomass is considered a kind of green energy because of its high efficiency and renewable, which has attracted extensive attention in electrode materials. So far, a variety of biomass resources, such as coffee grounds [4], cotton stalk [5], rice husk [6], have been used to synthesize electrode materials for supercapacitors.

The process of preparing activated carbon by biomass precursor mainly includes carbonization and activation. The precursor material is pyrolyzed in an inert atmosphere at a medium-high temperature (300-800 ℃). There are three processes to produce activated carbons: physical activation, chemical activation and physical-chemical activation. The activator for physical activation is usually CO2 and H2O because it uses the oxidizing property of the medium to react with the macromolecules in the carbonized material to open the blocked pores; it can also make the C atoms in the active site of the carbonized material and the O atoms in the medium generate reaction to generate new pores or expand the original pores. Chemical activation is a process in which chemical reagents such as KOH, K2CO3, H3PO4, ZnCl2 and alkali metal oxides are mixed with carbon rich precursors in a certain proportion and activated under the protection of inert gas and high temperature. The physical-chemical activation usually first mixes the biomass raw material with a chemical activator, and then introduces steam or CO2 gas as the activation gas for physical activation to increase the specific surface area of the carbon material [7], [8].

Chemical activation is used in this work on the one hand based on a large number of previous studies, on the other hand because this method is simple, low cost, conducive to industrial production. Among all activators, ZnCl2 and KOH are the most widely used activators for the production of activated carbon. According to the research of ZnCl2 and KOH are used to produce activated carbon from wheat straw, it is found that, unlike KOH, ZnCl2 is distributed uniformly through precursor, thus preventing excessive activation [9]. Therefore, ZnCl2 can be used as an activator to control pore production better.

In this work, activated carbon was prepared by tobacco stalk biological waste and ZnCl2 as an effective activator with high added value. The obtained activated carbon material owned high specific capacitance, accompanied by good conductivity, which would be a promising electrode material for supercapacitors. The high performance was introduced by a high specific surface area, which could also enhance the properties of high adsorption capacity and fast adsorption speed. So this kind of activated carbon materials could be widely used in air purification, sewage purification, toxic substance adsorption and other production fields. Above all, recourses reusing tobacco stalk waste not only improves its own economic value, but also provides a new solution for other agricultural waste resource treatment.

2. Experimental details

The tobacco stalk core was originated from local tobacco production base, and used as the precursor. All of the reagents used for the preparation of carbon samples were analytical grades.

The activated carbon was prepared via a chemical activation method with tobacco stalk core as a carbon source and ZnCl2 as a chemical activation agent. In a typical synthesis process, tobacco straw core powder was pyrolyzed in tubular furnace at 550 ℃ for 2 h under N2 atmosphere. Then the obtained bio-chars were mixed with various ZnCl2 (ZnCl2 to precursor weight ratios of 1:1, 2:1 and 3:1). The homogenous composites of biochar and activator were placed onto a Nickel crucible and then transferred into a tubular furnace at 800 ℃ for 2 h under N2 atmosphere at a heating rate of 5 ℃·min-1. Finally, the as-prepared activated carbon was washed with 1 M HCl and then deionized water several times until reaching a neutral pH to ensure the complete removal of metallic Zinc, unreacted materials and inorganic salts. The tobacco stalk core starting material was labeled as “TSC”, and the resultant tobacco stalk core derived carbons have been denoted as “TSCAC-x”, in where the “x” represents ZnCl2 to precursor weight ratio. To prove the effect of activator, an activated carbon material was synthesized under the same conditions without using any activation agents, which was denoted as TSCAC. The activation conditions of each sample are shown in Table 1.

Table 1. The activation process of TSCAC samples

Sample name
Activation temperature / ℃
Activation time / min
Mass ratio (ZnCl2: precursor)

3. Material characterization and electrochemical measurements

The morphology and microstructure of the samples were recorded by scanning electron microscope (SEM, ULTRATM 55). Wide-angle powder X-ray diffraction (XRD) patterns were collected on an X-ray diffractometer (Ultima IV, Japan) with Cu Zn α radiation.

The working electrode was fabricated by mixing the active material, polytetrafluoroethylene (PTFE), and acetylene black with a weight ratio of 80:10:10 dispersed in ethanol. Subsequently, the slurry was coated onto nickel foam (effective coating area is 1×1 cm2), and then vacuum dried at 80°C overnight. Subsequently, the electrodes were pressed under 10 MPa. Cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD) analysis were run within the operation applied potential window ranges of –1.0 to 0.0 V. The electrochemical impedance spectroscopy (EIS) data is carried out within the frequency of 500 kHz to 0.01 Hz. The specific capacitances (Cs, F·g-1) were measured from the GCD curves applying equation.

4. Results and discussion

4.1. SEM analysis

Scanning Electron Microscope images of the TSCACs material were presented in Fig. 1. The original biochar (TSCAC) was underdeveloped with a smooth and flat surface (Fig. 1(a)). Compared with TSCAC, the surface of other TSCACs material became very rough, and the pore structure was significantly improved (Fig. 1(b), (c), (d)) after activation by ZnCl2. The morphology of TSCACs largely depends on the amount of ZnCl2. As shown in Fig. 1(b), there are only a few shallow cracks and some incomplete pores on the surface of the TSCAC-1 sample, when the mass ratio of ZnCl2 to carbon precursor was 1:1. The surface roughness of the TSCAC-2 sample is greatly increased, and it has a relatively complete and continuous porous structure (as shown in Fig. 1(c)), which is conducive to electrolyte penetration and continuous electrochemical applications. However, the porous structure of TSCAC-3 began to collapse and surface agglomeration and fragmentation appeared (Fig. 1(d)), when the mass ratio increased to 3:1. The damage of porous structure may be caused by excessive corrosion of ZnCl2. These results show that a proper zinc oxide activation concentration is beneficial to the formation of a complete and continuous porous structure. The continuous and complete porous structure can increase the effective ion contact area, while also allowing the electrolyte to penetrate through the surface until they reach the inside of the biochar electrode, which is beneficial to the electrochemical energy storage reaction [10].

Fig. 1. SEM images of a) TSCAC, b) TSCAC-1, c) TSCAC-2, d) TSCAC-3

SEM images of a) TSCAC, b) TSCAC-1, c) TSCAC-2, d) TSCAC-3

Fig. 2 shows the XRD patterns of TSCAC and TSCAC-2. It can be observed that two broad peaks locked at around 23.5° and 44.6°, which can be indexed to the (002) and (100) lattice planes of the disordered and graphitic carbon, respectively [11]. This indicates that the disordered structure in the amorphous carbon layer is caused by the randomly oriented hexagonal carbon layer, which is beneficial to the increase of the surface area. This finding indicates that the ZnCl2 activation process promotes a certain degree of graphitization, and confirms that TSCAC was successfully transformed into amorphous carbon and part of graphitic carbon through the activation and carbonization process [12].

Fig. 2. XRD patterns of TSCAC and TSCAC-2

XRD patterns of TSCAC and TSCAC-2

5. Electrochemical performance analysis

The electrochemical behavior of the tobacco straw core-based carbons were analyzed in 6 M KOH electrolyte within a three-electrode system in CHI 760E electrochemical workstation (Chenhua, China). The working electrode was prepared by pressing the biochar samples, acetylene carbon black, and PTFE (5 wt. %) binder on the nickel foam current collector at a ratio of 8:1:1. Platinum sheet and the Hg/HgO were used as the counter electrode and reference, respectively.

Fig. 3(a) is the CV curve diagram of TSCAC-X series samples at a scan rate of 10 mV s-1. All the CV curves display a relatively symmetric rectangular shape and display a good current response, signifying the TSCAC owns the energy-storage mechanism of electrochemical double-layer capacitance (EDLC) behavior. The physical phenomena of electrostatic storage occurring at the electrode-electrolyte interface. The nearly rectangular shape of CV also suggests reversible electro- chemical performance. The areas of the CV curves reflect the capacitance value. As a result, the capacitance of TSCACs electrodes decreases in the order of TSCAC-2 > TSCAC-3 > TSCAC-1 > TSCAC. The above results can be attributed to the continuous and complete porous structure and a large specific surface area (Fig. 1).

Fig. 3. Electrochemical characterization in 6 M KOH aqueous electrolyte in a three-electrolyte system: a) CV curve diagram of TSCACs samples, b) Constant current charge and discharge curve of TSCACs samples, c) Specific capacitance versus current densities for TSCACs samples

Electrochemical characterization in 6 M KOH aqueous electrolyte in a three-electrolyte system:  a) CV curve diagram of TSCACs samples, b) Constant current charge and discharge curve  of TSCACs samples, c) Specific capacitance versus current densities for TSCACs samples

As shown in Fig. 3(b), galvanostatic charge-discharge (GCD) profiles of all TSCAC-based electrodes had triangular symmetrical distribution recorded at 1 A g-1 current density, suggesting their quasi-EDLC characteristics. The lowest specific capacitance of 171.3 F·g-1 was recorded for TSCAC and slightly higher capacitance of 224.0 F·g-1 for TSCAC-1 (increase by 30.8 %). When the mass ratio of ZnCl2 chloride to precursor is 2:1 (TSCAC-2), it led to the 2-fold increase of the specific capacitance (342.0 F·g-1) in comparison to TSCAC. In contrast, the specific capacitance (294.1 F·g-1) of TSCAC-3 was lower than TSCAC-2. TSCAC-2 exhibited the highest specific capacitance compared to other TSCACs samples, which is mainly attributed to the well-developed porosity of this sample and high specific surface area, which is consistent with the results in Fig. 1(c). These values were similar to the performance of biomass activated carbon reported in other studies, as shown in Table 3.

From Fig. 3(c) and Table 2, it can be seen that the electrochemical properties of the activated carbon with the increase of ZnCl2 amount show a trend of first increasing and then decreasing. TSCAC-2 samples show the maximum specific capacitance in the test range, and the specific capacitance retention at 10 A·g-1 is 84.2 % compared with that at 1 A·g-1, showing good rate performance.

Table 2. The comparing capacitance (Cm) of all TSCAC samples

Cm / (F/g)
I d =   0.5 A/g
I d =   1 A/g
I d = 2 A/g
I d = 3 A/g
I d = 5 A/g
I d = 10 A/g

Table 3. Comparison of the electrochemical performance of biomass activated carbon reported in this study and other literature

Activating agent
Current density (A·g-1)
Specific capacitance (F·g−1)
Lotus seed
1 M H2SO4
Pomelo peels
Tobacco stalks core
This work

6. Conclusions

The effect of mass ratio of tobacco stalk core to ZnCl2 on the electrochemical performance of activated carbon has been systematically studied. The experimental results show that TSCAC-2 was the optimal material, which has uniform porous structures, high surface areas and perfect graphite structure. And TSCAC-2 displays high rate capabilities and high specific capacitance (up to 342.0 F·g-1 at 1 A·g-1 current density), it still can maintain a high capacitance of 288.0 F·g-1 at 10 A·g-1 current density. The results demonstrated that the tobacco stalk core carbons herein to be promising electrode materials. The methodology adopted herein also provides a new approach to obtain porous carbon materials from waste biomass, which may be extended to other sources, such as straw, bark and so on.


This work was financially supported by grants from Guangdong Tobacco Monopoly Administration Science and Technology programs (No. 2019011).


  1. K. Nanaji, B. V. Sarada, U. V. Varadaraju, T. N. Rao, and S. Anandan, “A novel approach to synthesize porous graphene sheets by exploring KOH as pore inducing agent as well as a catalyst for supercapacitors with ultra-fast rate capability,” Renewable Energy, Vol. 172, pp. 502–513, Jul. 2021, [Publisher]
  2. K. Cong, F. Han, Y. Zhang, and Q. Li, “The investigation of co-combustion characteristics of tobacco stalk and low rank coal using a macro-TGA,” Fuel, Vol. 237, pp. 126–132, Feb. 2019, [Publisher]
  3. Z. Huang et al., “Research on high-value utilization of carbon derived from tobacco waste in supercapacitors,” Materials, Vol. 14, No. 7, p. 1714, Mar. 2021, [Publisher]
  4. M. Biegun, A. Dymerska, X. Chen, and E. Mijowska, “Study of the active carbon from used coffee grounds as the active material for a high-temperature stable supercapacitor with ionic-liquid electrolyte,” Materials, Vol. 13, No. 18, p. 3919, Sep. 2020, [Publisher]
  5. J. Cheng, S.-C. Hu, G.-T. Sun, K. Kang, M.-Q. Zhu, and Z.-C. Geng, “Comparison of activated carbons prepared by one-step and two-step chemical activation process based on cotton stalk for supercapacitors application,” Energy, Vol. 215, p. 119144, Jan. 2021, [Publisher]
  6. X. He, P. Ling, M. Yu, X. Wang, X. Zhang, and M. Zheng, “Rice husk-derived porous carbons with high capacitance by ZnCl2 activation for supercapacitors,” Electrochimica Acta, Vol. 105, pp. 635–641, Aug. 2013, [Publisher]
  7. K. Köse, B. Pişkin, and M. K. Aydınol, “Chemical and structural optimization of ZnCl2 activated carbons via high temperature CO2 treatment for EDLC applications,” International Journal of Hydrogen Energy, Vol. 43, No. 40, pp. 18607–18616, Oct. 2018, [Publisher]
  8. J. Pallarés, A. González-Cencerrado, and I. Arauzo, “Production and characterization of activated carbon from barley straw by physical activation with carbon dioxide and steam,” Biomass and Bioenergy, Vol. 115, pp. 64–73, Aug. 2018, [Publisher]
  9. Y. Ma, “Comparison of activated carbons prepared from wheat straw via ZnCl2 and KOH activation,” Waste and Biomass Valorization, Vol. 8, No. 3, pp. 549–559, Apr. 2017, [Publisher]
  10. M. Inagaki, M. Toyoda, Y. Soneda, S. Tsujimura, and T. Morishita, “Templated mesoporous carbons: synthesis and applications,” Carbon, Elsevier BV, 2016. [Publisher]
  11. Y. Li et al., “Green conversion of bamboo chips into high-performance phenol adsorbent and supercapacitor electrodes by simultaneous activation and nitrogen doping,” Journal of Analytical and Applied Pyrolysis, Vol. 155, p. 105072, May 2021, [Publisher]
  12. A. A. Mohammed, C. Chen, and Z. Zhu, “Low-cost, high-performance supercapacitor based on activated carbon electrode materials derived from baobab fruit shells,” Journal of Colloid and Interface Science, Vol. 538, pp. 308–319, Mar. 2019, [Publisher]
  13. R. L. Shrestha et al., “Nanoarchitectonics of lotus seed derived nanoporous carbon materials for supercapacitor applications,” Materials, Vol. 13, No. 23, p. 5434, Nov. 2020, [Publisher]
  14. J. Ai et al., “Corncob cellulose-derived hierarchical porous carbon for high performance supercapacitors,” Journal of Power Sources, Vol. 484, p. 229221, Feb. 2021, [Publisher]
  15. H. Lin, Y. Liu, Z. Chang, S. Yan, S. Liu, and S. Han, “A new method of synthesizing hemicellulose-derived porous activated carbon for high-performance supercapacitors,” Microporous and Mesoporous Materials, Vol. 292, p. 109707, Jan. 2020, [Publisher]