Finite element analysis on the response of 6061-T 6 aluminum alloy tubes with a local sharp cut under cyclic bending

In this paper, the finite element software ANSYS Workbench 14.0 is used to analyze the moment-curvature and ovalization-curvature relationships of 6061-T6 aluminum alloy tubes with a local sharp cut under curvature-controlled symmetrical cyclic bending. The cut depths of 0.4, 0.8, 1.2, 1.6 and 2.0 mm were considered. The experimental moment-curvature relationship exhibited an almost steady loop from the beginning of the first cycle; the cut depth had almost no influence on the curves. Moreover, the ovalization-curvature curve increased in an increasing, unsymmetrical and ratcheting manner with the number of bending cycles. Large cut depths resulted in larger ovalization of the tube cross-section. The ANSYS analysis was compared with the experimental finding. The simulated results exhibited close correspondence to those obtained from the experiments.


Introduction
It is well known that the bending of circular tubes results in the ovalization (change in the outer diameter divided by the original outer diameter) of the tube cross-section.This ovalization increases slowly during reverse bending and continuous cyclic bending and, in turn, results in the deterioration of the circular tube, which buckles when the ovalization reaches some critical value.The circular tube is severely damaged during buckling and cannot bear the load, which ultimately results in obstruction and leakage of the material being transported.As such, a complete understanding of the response of the circular tube to cyclic bending is essential for industrial applications.
As part of the earliest research regarding this issue, Shaw and Kyriakides [1] designed and constructed a tube cyclic bending machine and conducted a series of experimental and theoretical investigations.Kyriakides and Shaw [2] later investigated the inelastic behavior of tubes subjected to cyclic bending and extended the analysis of tubes to stability conditions under cyclic bending.Corona and Kyriakides [3] investigated the stability of tubes subjected to combined bending and external pressure; they also later [4] studied the degradation and buckling of tubes under cyclic bending and external pressure.Corona and Vaze [5] studied the response, buckling, and collapse of long, thin-walled seamless steel square tubes under bending, and later they [6] experimentally investigated the elastic-plastic degradation and collapse of steel tubes with square cross-sections under cyclic bending.Corona and Kyriakides [7] also studied the asymmetric collapse modes of pipes under combined bending and pressure.Corona et al. [8] conducted a set of bending experiments on aluminum alloy tubes to investigate the yield anisotropy effects on buckling.Later, Kyriakides et al. [9] studied the plastic bending of steel tubes with a diameter-to-thickness ratio ( / ratio) of 18.8, exhibiting Lüders bands through the experiment.Limam et al. [10] studied the inelastic bending and collapse of tubes in the presence of bending and internal pressure.Later, Limam et al. [11] later investigated the collapse of dented tubes under combined bending and internal pressure.Bechle and Kyriakides studied the localization in NiTi tubes under bending [12].
Additionally, other scholars have published a number of related studies.Elchalakani et al. [13] experimentally conducted tests on different / ratios of grade C350 steel tubes under pure bending and proposed two theoretical simulation models.Jiao and Zhao [14] tested the bending behavior of very high strength circular steel tubes and proposed a plastic slenderness limit.Houliara and Karamanos [15] investigated the buckling and post-buckling of long-pressurized, elastic, thin-walled tubes under in-phase bending.Elchalakani et al. [16] conducted the variable amplitude, cyclic, pure bending tests to determine fully ductile section slenderness limits for cold-formed CHS.Mathon and Liman [17] experimentally studied the collapse of thin, cylindrical shells that were submitted to internal pressure and pure bending.Elchalakani and Zhao [18] investigated concrete-filled, cold-formed circular steel tubes that were subjected to variable amplitude, cyclic, pure bending.Fatemi et al. [19] discussed the parameters that affect the buckling and post-buckling behavior of high strength pipelines under bending.Yazdani and Nayebi [20] discussed the ratcheting and fatigue damage of thin-walled tubes under cyclic bending and steady internal pressure.Jiang et al. [21] experimentally investigated and designed the thin-walled concrete-filled steel tubes under Bending.Shariati et al. [22] experimental studied the SS316 cantilevered cylindrical shells subjected to cyclic bending.
In 1998, Pan et al. [23] designed and set up a new measurement apparatus.It was used with the cyclic bending machine to study various kinds of tubes under different cyclic bending conditions.For instance, Pan and Her [24] investigated the response and stability of 304 stainless steel tubes that were subjected to cyclic bending with different curvature-rates, Lee et al. [25] studied the influence of the / ratio on the response and stability of circular tubes that were subjected to symmetrical cyclic bending, Lee et al. [26] experimentally explored the effect of the / ratio and curvature-rate on the response and stability of circular tubes subjected to cyclic bending, and Chang and Pan [27] discussed the buckling life estimation of circular tubes subjected to cyclic bending.
In practical industrial applications, tubes are in hostile environments, so the material in the environment may corrode the tube surface and produce notches.Additionally, when using a tube, it must have a notch design.The mechanical behavior and buckling failure of a notched tube differs from that of a tube with a smooth surface.In 2010, Lee et al. [28] studied the variations in ovalization that occur in sharp-notched circular tubes subjected to cyclic bending.Lee [29] later investigated the mechanical behavior and buckling failure of sharp-notched circular tubes under cyclic bending, and Lee et al. [30] experimentally discussed the viscoplastic response and collapse of sharp-notched circular tubes subjected to cyclic bending.It is known that the tubes may be damaged by a sharp object during the delivery, installation or use.Once a local sharp cut is on a tube (Fig. 1(c)), the response of the tube under cyclic bending should be different from that of a smooth or other kind of notched tube under cyclic bending.
Therefore, the response of tubes with a local sharp cut under cyclic bending is investigated in this paper.

Experiment
The experiments were performed in a specially built testing apparatus, which is shown schematically in Fig. 2(a).This apparatus was designed for conducting the bending, reverse, and cyclic bending test and detailed descriptions thereof are provided elsewhere [24][25][26][27][28]. Pan et al. [23] designed a light-weight instrument, shown schematically in Fig. 2(b), for measuring the curvature and ovalization of the tube cross section.The two side inclinometers measure the angle changes during cyclic bending and the curvature of the tube can be determined through a simple mathematical calculation (extended version of the instrument and the calculation are described in Pan et al. [23]).Circular tubes made of 6061-T6 aluminum alloy were used in this study.Table 1 shows the alloy's chemical composition.The ultimate stress was 258 MPa, the 0.2 % strain offsetting the yield stress ( ) as 166 MPa, and the percent elongation was 23 %.The raw, unnotched 6061-T6 aluminum alloy tubes had an outside diameter of 35.0 mm, a wall thickness of 3.0 mm and a tube length of 50 mm.The raw tubes were machined on the outside surface to obtain the desired shape and depth of the sharp cut.Fig. 3(a) shows a schematic drawing of the tube with a sharp cut where the cut depth is denoted as .In this study, five different cut depths were considered including 0.4, 0.8, 1.2, 1.6 and 2.0 mm, respectively.The cut root radius for all tested tubes was controlled to be less than 1/100 mm and all tested tubes were carefully examined before the test.Fig. 3(b) shows a picture of the tested 6061-T6 aluminum alloy tubes with different cut depths.The bending experiments were performed under curvature-controlled conditions and curvatures were applied at loading curvature rates of 0.03 m -1 /s.The two load cells installed in the testing apparatus (Fig. 2(a)) were used to measure the bending moment.Moreover, the light-weight instrument (Fig. 2(b)) was used to measure the curvature and ovalization of the tube cross-section.

Finite element analysis
A uniaxial cyclic stress-strain curve was constructed multilinearly in ANSYS shown in Fig. 4(b) according to the tested uniaxial cyclic stress-strain curve for 6061-T6 aluminum alloy shown in Fig. 4(a).Additionally, the kinematic hardening rule was used for cyclic loading.Owing to the three-dimensional geometry and elastoplastic deformation of the tube, the SOLID 185 element was used for relative analysis.This element is a tetrahedral element built in ANSYS, which is suitable for analyzing plastic and large deformations.In particular, this element is adequate for analyzing shell components subjected to bending.Moreover, owing to the right-left symmetry, only half of the tube model was constructed.Fig. 5 shows the mesh constructed by ANSYS.
Fig. 5. Mesh constructed by ANSYS for half tube Fig. 6(a) shows the restrictions on the symmetrical plane (central cross section), constructed by ANSYS, for a tube subjected to cyclic bending.Since the tubes were bent in the -direction only, the frictionless roller support was fixed to the symmetrical plane and the displacement in the -direction of this plane was set to zero.Fig. 6(b) shows the loading condition constructed by ANSYS on the basis of the tube bending device.As the figure shows, the remote displacement in the -direction was unrestricted, i.e., the rotation was free to move in the -direction.In addition, the bending moment was applied only in the -direction and hence, the rotations in the -and -directions were set to zero.The rotation angle in the -direction (Fig. 7) was used as the input data for the tube subjected to curvature-controlled cyclic bending and is related to the curvature through: where is the radius of curvature and is the original tube length.is the outside diameter and Δ is the change in the outside diameter.It can be seen that the ovalization increases in a ratcheting and unsymmetrical manner with the number of bending cycles.A higher value of for the cut tube causes greater ovalization in the tube's cross-section.In addition, higher values of for sharp-notched SUS304 stainless steel tubes led to more severe unsymmetrical trends in the Δ ⁄ -⁄ curve.This phenomenon of Δ ⁄ -⁄ curves is similar to that for local sharp-notched SUS304 stainless steel tubes subjected to cyclic bending [31].But the unsymmetrical trend of Δ ⁄ -⁄ curves for local sharp-cut 6061-T6 aluminum alloy tubes is more significant than that for local sharp-notched SUS304 SUS304 stainless steel tubes.Figs.10(a

Conclusions
The response of local sharp-cut 6061-T6 aluminum alloy tubes with different cut depths subjected to cyclic bending were investigated in this study.On the basis of the experimental and theoretical results, the following conclusions can be drawn: 1) The ⁄ -⁄ curves of local sharp-cut 6061-T6 aluminum alloy tubes with any cut depth exhibit a steady loop from the first cycle under curvature-controlled cyclic bending.In addition, the stable ⁄ -⁄ loops have very similar shape and size irrespective of the cut depth.
2) The Δ ⁄ -⁄ curves show that the ovalization of the tube cross section increases in a ratcheting manner with increasing number of cycles.Higher leads to more unsymmetrical trends and larger ovalization of the tube cross-section compared with those obtained at lower values of .
3) Using adequate stress-strain relationships, mesh, boundary conditions, and loading conditions, the finite element software ANSYS can simulate the behavior of local sharp-cut circular tubes subjected to cyclic bending; this behavior includes the moment-curvature and ovalization-curvature relationships.The simulated results exhibited close correspondence to those obtained from experiments.

Fig. 1 .
Pictures of a) a tube with a circumferential sharp notch, b) a tube with a local sharp notch and c) a tube with a local sharp cut However, all investigations of the sharp notch were the circumferential sharp notch as shown in Fig.1(a).If the sharp notch is a local sharp notch (Fig.1(b)), the response of a local sharp notch tube under cyclic bending should be different from that of a circumferential sharp notch tube under cyclic bending.Therefore, Lee et al.[31] investigated the response of local sharp-notched circular tubes with different notch depths subjected to cyclic bending.

Fig. 2 .
a) A schematic drawing of the bending device, b) a schematic drawing of the curvature-ovalization measurement apparatus

Fig. 3 .
a) A Schematic drawing of a tube with a sharp-cut depth of , b) a picture of the tested 6061-T6 aluminum alloy tubes with different cut depths

Fig. 4 .
(a) Tested and (b) ANSYS constructed data of the uniaxial cyclic stress-strain curves for 6061-T6 aluminum alloy

Fig. 6 .
a) Restrictions on the symmetrical plane constructed by ANSYS, b) loading condition constructed by ANSYS

Fig. 7 .Fig. 9 .
Fig. 7. Relationship between rotating angle and curvature for a tube under pure bending4.Comparison of the experimental and ANSYS analysis resultsFig.8(a) shows a typical set of experimentally determined cyclic moment ( ⁄ )-curvature ( ⁄ ) curves for local sharp-cut 6061-T6 aluminum alloy tubes, with cut depth of 0.4 mm, subjected to cyclic bending.The moment and curvature were normalized by and ⁄ , respectively (Corona and Kyriakides[3,4]).The tubes were cycled between